My licence effort to make gold

As you can see making gold according to the licence is relatively simple ?!
just the right temp and some air...

----- Original Message -----
From: Hans S
To: Dr. Champion
Sent: Tuesday, June 29, 2010 12:47 PM
Subject: Help needed for getting resonance




Hello Dr.C

Had my first run the last 4 days with this setup:






Air Temp setting 294 to 297C for getting 291C in Alu pipe ('boat').

Hysteresis set to 1C

After 1 day 295C was needed for getting 291 into the Alu. Stable 291C for 3 days(mass helps...).

Square Alu pipe 10cm length 25cm, 4mm thick. With 16mm Alu base plate. Total mass: 1.4Kg

Tubing covered with alu foil after putting the silver bar in.

Air heating spiral made of 12mm tubing, 6 meters.



Used K type sensors (NiCr-Ni , - 50 to +400 °C) small(3mm)&fast :0.3sec.

Klass 2 deviation: 291Cx0.0075 =+/- 2 C

Sensors 2-3cm into the Alu (holes drilled)



Air pump adjustable from 1 to 9 liters a min. 2 used.












Silver 250gr after 100Hours, no gold formation according to gold tester Mizar M24

Small discoloration of the silver, easy to be wiped away (see middle )



So Dr.C no result so far.

Need more precise sensors? No solid Alu(1.4 kg not enough?)for the ‘boat’? ,

Need to use thin household foil(with enough mass)? Less space between silver and Alu?



Hans

Amsterdam

The Netherlands


His answer:

From: Dr. Champion
To: Dr. Champion
Sent: Tuesday, June 29, 2010 4:25 PM
Subject: My analysis of Hans first test and suggestions.




Everything appears to be totally proper except for the silver resonance. It is obvious that the Al temperature and resonance is working within his kiln. This is obvious from the discoloration of his silver. Allow me to explain this phenomenon. The discoloration occurs from two occurrences’. First there is a slight positive resonance in the reactor with a weak coupling of the resonance to the silver. The coloration of the bar is due to this resonance and the positive air flow, Atmospheric air is ~80% nitrogen and this action on VAu will produce the color. Also remember the resonance coming out of the Al tubing.



Simple practically if the resonance is not directly coupled to the silver a damping effect will occur. This is one of the reasons I have used Al foil because it is not rigid. Now you can use Al foil within a rigid Al container but the Al foil appears to couple to rigid silver more effectively. Hans setup is very professional and all that is required now is a stronger resonance in the bar.



Think of it as a tuning fork and you want to resonate the bar as strongly as possible.



Dr. Champion





Later i tried several diffent setups but no succes...
only my power company is happy with the 1000kWh of experimenting...


have still contact with other unsuccesfull licence members who are still hopefull to receive usefull tech info?!

Dr. Champion is gone phishing for new capital ?

Gone fishing, back in a couple of weeks.
Dr. Champion

see March 25, 2011

$6000 goldmaking licence for free!

In may 2010 I was convinced that Dr.C was after all those years did finally find the gold making way. I did greedy buy a licence. Here is wat he send me (inc. his spelling errors)(you are free to use this $6000 info to produce gold..:):



Every thing started of slow do to a major discovery it is time to start everything up now.

Most of you realize of my attack last year and I reported vision issues. You will be receiving emails from Ms. Anndrea Horton from time to time and if you need to contact me please feel free to contact here directly. Now here is some science that will get you started.

Prior to starting it is not a requirement but I would appreciate pictures of your progress especially when you start gold production. You name will never be released but only four country.

You received the Gold formation short version

What you see here is specificallythe resonant temperature for aluminum. The resonance temperature for aluminum is 291 C.

This temperature has been known for years but this is not sufficient by itself.

The most recent advancement is the addition of nitrogen and it is easily attainable from the atmosphere the form of air flow.

This is the big dark secret that you have been waiting for.

I put the bars in the following configuration





The above configuration is a aluminum pan made from easily attainable foil. See the next step



The above is the pan with 3 10 ounce silver bars inside the furnace the aluminum tubing goes through the furnace wall and supplies the atmospheric air.

Flowing is how the air enters the tubing.





An aluminum is placed over the aluminum boat housing the silver.

The temperature is set between 292-303 C

The length of reaction time is between 48 to 60 hours.





This is what the bars look like after 48 hours.

I had a technician drill a 150 miligram sample and the following is the result after 20% HNO3.







What you are observing above in the two pictures is very pure gold.

IMPORTRANT NOTE

Without the constant flow of atmospheric air there there is little to no gold formation. You will form a VAu which stands for virtual gold a termed coined from Clemson University on my research.

The flow of air needs to be ar a rate that will allow for the toal temperature to remain at the 291C. If the temperature is to high you will start to produce titanium.

There will be more pictures in 48 hours with results of actual production.

Dr. Champion